UHMW-PE Fender pads and fenders are produced by a sintering process either from virgin or from reclaimed material (aprox. 70% reclaimed +30% virgin material - also named double-sintered or blended UHMW-PE).
UHMW-PE (UltraHighMolecularWeight-PolyEthylene) combines highest strength with wear resistance and consequently provides the best durabilty of all available Polyethylene products.
The UHMW-PE Fender pads advantages are:
Very high impact strength
Very low friction coefficient
Very high abrasion resistance
UV + Ozone resistant
Non-conducting (optional)
100% recycable, non-rottening
Cut to size sheet ,all size is available with us
Standard colour :Black ,Yellow ,Blue ,Green ,Red,White ,other colour is available upon request .
The UHMW-PE Fender pads application is as follows:
low resistance sliding plates on fender panels
low resistance slinding panels for bridge and pier protection
corner protection for offshore structures, berths and other marine facilities
| project | unit | Test Methods | index | |
General Physical Properties |
molecular weight | X10 | GB184-80ASTMD4020-81 | 50-1080 |
| density | g/cm3 | GB1033-86 | 0.93-0.98 | |
| Volatile matter (moisture) | % | GB2914-82 | ≤0.15 | |
| Izod impact strength | KJ/m2 | GB1843-80 | not broken | |
| impact strength of beam | KJ/m2 | GB1043-86 | 80-130 | |
| Tensile breaking strength | Mpa | GB1040-79 | 25-40 | |
| Tensile elongation at break | % | GB1040-79 | 50-600 | |
| thermal performance | Melting point | ºC | ASTMD 2117 | 136 |
| Vicat softening point | ºC | ASTMD 2117 | 80 | |
| embrittlement temperature | ºC | ASTMD1525 | ≤-70 | |
| Linear expansion coefficient | 10-5/ºC | ASTMD 696 | 0.15 | |
| Thermal deformation temperature 0.45Mpa | ºC | ASTMD 648 | 110 | |
| Electric energy | volume resistivity | ASTMD 257 | 1017~ 1018 | |
| Dielectric strength | KV/mm | ASTMD 149 | 50 | |
| Dielectric constant | 106Hz | ASTMD 150 | 2.30 | |
| Dielectric loss tangent | 106Hz | ASTMD 150 | ≤5×10-4 |
We offer excellent sliding properties and abrasion/wear resistance due to its low coefficient of friction. HDPE Sheet is very tough and impact resistant, even at low temperatures, it is lightweight, easy to weld but difficult to bond. As a thermoplastic sheet manufacturer in China, Abosn can supply both single color and Dual-color HDPE sheets to suit customer demands. We own the most advanced Extrusion machines to extrude HDPE sheets with fixed material under certain pressure and temperature. HDPE Sheet has an almost waxy feel to it and is pretty good at being a low friction wear strip material and is used probably more than any other plastic as a wear strip on conveyors or production lines of huge companies. While it is difficult to bond effectively to anything, which means that HDPE Sheet will need to be physically or mechanically fixed in place using screws etc.